Vat Photopolymerization of CeO2-Incorporated Hydrogel Scaffolds with Antimicrobial Efficacy

We herein demonstrate the utility of gelatin methacryloyl (GelMA)/poly(ethylene glycol) diacrylate (PEGDA)-cerium oxide (CeO₂) hydrogel inks for manufacturing hydrogel scaffolds with antimicrobial efficacy by vat photopolymerization. For uniform blending with GelMA/PEGDA hydrogels, CeO₂ nanoparticles with a round shape were synthesized by the precipitation method coupled with calculation at 600 °C. In addition, they had highly crystalline phases and the desired chemical structures (oxidation states of Ce³⁺ and Ce⁴⁺) required for outstanding antimicrobial efficacy. A range of GelMA/PEGDA-CeO₂ hydrogel scaffolds with different CeO₂ contents (0% <i>w</i>/<i>v</i>, 0.1% <i>w</i>/<i>v</i>, 0.5% <i>w</i>/<i>v</i>, 1% <i>w</i>/<i>v</i>, and 5% <i>w</i>/<i>v</i> with respect to distilled water content) were manufactured. The photopolymerization behavior, mechanical properties, and biological properties (swelling and biodegradation behaviors) of hydrogel scaffolds were characterized to optimize the CeO₂ content. GelMA/PEGDA-CeO₂ hydrogel scaffolds produced with the highest CeO₂ content (5% <i>w</i>/<i>v</i>) showed reasonable mechanical properties (compressive strength = 0.56 ± 0.09 MPa and compressive modulus = 0.19 ± 0.03 MPa), a high swelling ratio (1063.3 ± 10.9%), and the desired biodegradation rate (remaining weight after 28 days = 39.6 ± 2.3%). Furthermore, they showed outstanding antimicrobial efficacy (the number of colony-forming units = 76 ± 44.6 (×10³)). In addition, macroporous GelMA/PEGDA-CeO₂ hydrogel scaffolds with tightly controlled porous structures could be manufactured by vat photopolymerization.