Continuous Cooling Transformation of Tool Steels X153CrMoV12 and 100MnCrW4: Analysis of Microstructure and Hardness Changes

The aim of this work is to perform a detailed dilatometric analysis of the decomposition of austenite during the cooling process using experimentally derived continuous cooling transformation (CCT) diagrams for two specific tool steels, X153CrMoV12 Bohdan Bolzano, Bratislava, Slovakia and 100MnCrW4. The dilatometric curves were compared with metallographic evaluations using scanning electron microscopy (SEM). In addition, hardness measurements were performed to obtain additional information about the mechanical properties of the materials. All experimental work was performed using a DIL 805A. The accuracy of the resulting CCT diagrams was verified by comparing them with those calculated with the JMatPro software v12.4. The cooling rates ranged from 20 °C/s to 0.01 °C/s, depending on the specific type of steel tested. The novelty of this research is the combination of experimental and simulation methods to analyze the influence of alloying elements on the kinetics of phase transformations in tool steels. It was found that one of the most significant factors affecting the CCT diagrams is the weight percentage of alloying elements in the steels. These results clearly show that increasing the weight percentage of the content of alloying elements has a significant impact on the accuracy of the simulation results derived from the JMatPro software.