Effect of Sinter Temperature and Thermochemical Coating on Mechanical Properties of Ti₆Al₄V Produced by Powder Metallurgy

Ti 6 Al 4 V alloy is used in many areas such as aviation, space and biomaterials due to its high mechanical properties and low density. It has been widely studied in the literature due to its superior properties in engineering applications. Ti 6 Al 4 V, especially produced by powder metallurgy (PM), can be subjected to various surface coating processes after production. In this study, the effects of sintering temperature and thermochemical coating process on the microstructural and mechanical properties of Ti 6 Al 4 V alloy were investigated. The microstructural changes of the alloy sintered at 800 ∘ C, 1000 ∘ C and 1200 ∘ C were analyzed. Since the best mechanical properties were obtained at 1200 ∘ C, coating with Ekabor-II (90% SiC, 5% B 4 C, 5% KBF 4 ) was applied to the sample produced at this temperature. SEM and EDX analyses showed parameter changes in [Formula: see text] and [Formula: see text] phases and the formation of boron and carbide phases such as TiB, TiB 2 , TiC, SiC and B 4 C. Mechanical tests revealed that sintering temperature and boron treatment significantly increased hardness, tensile and compressive strength. The results show that high sintering temperatures and thermochemical coatings enable Ti 6 Al 4 V to be developed for high-performance applications.