Hybrid Tool Holder by Laser Powder Bed Fusion of Dissimilar Steels: Towards Eliminating Post-Processing Heat Treatment

The hybridization of additive manufacturing (AM) with conventional manufacturing processes in tooling applications allows the customization of the tool. Examples include weight reduction, improving the vibration-dampening properties, or directing the coolant to the critical zones through intricate conformal cooling channels aimed at extending the tool life. In this regard, metallurgical challenges like the need for a post-processing heat treatment in the AM segment to meet the thermal and mechanical properties requirements persist. Heat treatment can destroy the dimensional accuracy of the pre-manufactured heat-treated wrought segment, on which the AM part is built. In the case of dissimilar joints, heat treatment may further impact the interface properties through the ease of diffusional reactions at elevated temperatures or buildup of residual stresses at the interface due to coefficient of thermal expansion (CTE) mismatch. In this communication, we report on the laser powder bed fusion (L-PBF) processing of MAR 60, a weldable carbon-free maraging powder, to manufacture a hybrid tool holder for general turning applications, comprising a wrought segment in 25CrMo4 low-alloy carbon-bearing tool steel. After L-PBF process optimization and manipulation, as-built (AB) MAR 60 steel was characterized with a hardness and tensile strength of ~450 HV (44–45 HRC) and >1400 MPa, respectively, matching those of pre-manufactured wrought 25CrMo4 (i.e., 42–45 HRC and 1400 MPa). The interface was defect-free with strong metallurgical bonding, showing slight microstructural and hardness variations, with a thickness of less than 400 µm. The matching strength and high Charpy V-notch impact energy (i.e., >40 J) of AB MAR 60 eliminate the necessity of any post-manufacturing heat treatment in the hybrid tool.