Corrosion Behavior of X65 API 5L Carbon Steel Under Simulated Storage Conditions: Influence of Gas Mixtures, Redox States, and Temperature Assessed Using Electrochemical Methods for up to 100 Hours

In the context of the deep geological disposal of high-level and intermediate-level long-lived radioactive waste in France, the Callovian–Oxfordian (Cox) clay formation has been selected as a natural barrier. Thus, understanding the corrosion phenomena between the carbon steel used (API 5L X65) for the waste lining tubes and the Cox pore water, as well as its possible future evolutions, is of great importance. A controlled laboratory experiment was conducted using robust handmade API 5L X65 carbon steel electrodes in synthetic Cox pore water under equilibrium with three distinct gas atmospheres, simulating oxic, anoxic, and sulfide-rich environments at 25 °C and 80 °C, in a batch-type electrochemical cell. The experimental methodology involved linear polarization resistance (LPR) cycles, electrochemical impedance spectroscopy (EIS), and Tafel extrapolation at regular intervals over a period of 70 to 100 h to elucidate corrosion mechanisms and obtain corrosion current densities. At the same time, the fluid’s key geochemical parameters (temperature, pH, and redox potential) were monitored for temporal variation. This study, with results showing high corrosion rates under the three conditions investigated at two temperatures, underscores the importance of controlling the immediate environment of the containment materials to prevent exposure to variable conditions and to ensure that corrosion remains controlled over the long term.