Nanostructured TiNi Wires for Textile Implants: Optimization of Drawing Process by Means of Mechano-Chemical Treatment

TiNi-based alloys are widely utilized in various engineering and medical applications. This study presents a newly developed and optimized technology for producing TiNi wires with a diameter of 40 μm utilizing a combined mechano-chemical treatment and drawing process. The resulting thin wires were tested and characterized using multiple methods to determine their structural, phase, and mechanical properties. The structure of the TiNi wires, designed for use as textile implants in reconstructive medicine, features a TiNi metal matrix (B2 and B19′ phases) at the core and a surface oxide layer. A key structural characteristic of these wires is the presence of fine nanograins averaging 15–17 nm in size. No texturizing of the metallic material was observed during repeated plastic deformations throughout the drawing process. The applied mechano-chemical treatment aimed to modify the structure of the wires’ surface oxide layer. Specifically, reducing the thickness and roughness of this layer decreased the friction coefficient of the alloy during drawing, thus significantly reducing the number of breaks during production. At the same time, the cryogenic treatment of the final product was found to stabilize the martensitic phase B19′, which reduces the Young’s modulus by 10 GPa. Consequently, this newly developed methodology enhances the material’s quality and reduces labor costs during production.