Easy formation of AuPt nanoalloys on chitosan films and their synergistic effects in the catalyzed reduction of p-nitrophenol and hydrolysis of ammonia-borane

AuPt bimetallic nanoparticles supported on chitosan films were successfully obtained via a co-adsorption and co-reduction approach, supported by the excellent ability of chitosan to interact with and retain Au 3 + and Pt 2+ ions. The protocol enables the production of mostly spherical mono- and bimetallic nanoparticles , featuring average diameters ranging between 2.0 and 3.0 nm while maintaining narrow size distributions. The catalytic properties of nanocomposites were tested via the reduction of 4-nitrophenol (4-NP) and confirmed by the hydrolysis of ammonia borane (AB). The catalytic response of bimetallic samples was significantly higher than monometallic ones, with kinetic constants 5.0 and 3.0 times greater for 4-NP reduction and AB hydrolysis, respectively, alongside higher conversions (> 95 %) and turn-over frequency (TOF) values. Since all specimens exhibited similar metal content (⁓10 w/w %) and comparable nanoentities in size, morphology, and dispersion, the above results could be associated with an electronic synergism originating from the alloying process, enhancing the rate of limiting steps in both reactions. Additionally, the use of chitosan as support facilitates easy catalyst recovery , enabling its use for up to five successive catalytic runs without showing a noticeable decline in performance. • AuPt nanoalloys formed on chitosan films using a straightforward methodology. • Biobased nanocomposites with enhanced catalytic activity owing to synergistic effects. • Chitosan support enables the effective reusability of the catalyst in multiple runs. • Samples catalyzed the reduction of p-nitrophenol and the ammonia-borane hydrolysis.