Viscoelastic, Shape Memory, and Fracture Characteristics of 3D-Printed Photosensitive Epoxy-Based Resin Under the Effect of Hydrothermal Ageing

Using 3D-printed (3DPd) polymers and their composites as shape memory materials in various smart engineering applications has raised the demand for such functionally graded sustainable materials. This study aims to investigate the viscoelastic, shape memory, and fracture toughness properties of the epoxy-based ultraviolet (UV)-curable resin. A UV-based DLP (Digital Light Processing) printer was employed for the 3D printing (3DPg) epoxy-based structures. The effect of the hydrothermal accelerated ageing on the various properties of the 3DPd components was examined. The viscoelastic performance in terms of glass transition temperature (Tg), storage modulus, and loss modulus was evaluated. The shape memory polymer (SMP) performance with respect to shape recovery and shape fixity (programming the shape) were calculated through dynamic mechanical thermal analysis (DMTA). DMTA is used to reveal the molecular mobility performance through three different regions, i.e., glass region, glass transition region, and rubbery region. The shape-changing region (within the glass transition region) between the Tg value from the loss modulus and the Tg value from the tan(δ) was analysed. The temperature memory behaviour was investigated for flat and circular 3DPd structures to achieve sequential deployment. The critical stress intensity factor values of the single-edge notch bending (SENB) specimens have been explored for different crack inclination angles to investigate mode I (opening) and mixed-mode I/III (opening and tearing) fracture toughness. This study can contribute to the development of highly complex shape memory 3DPd structures that can be reshaped several times with large deformation.