Femto-second Laser’s Enabling New Length Scale Fabrications for Rapid Post Irradiation Examination of Materials: Concluding LDRD Project Poster

Mechanical testing campaigns are required to qualify materials for advanced reactor conditions, yet economical and safety limitations restrict the number of standardized mechanical tests that can be performed. Reducing the size of the sample is one approach to addressing these challenges and to accelerating testing. Previous research has shown that smaller mechanical test samples produce higher yield and ultimate stress values compared to values measured from standard sample sizes: the “smaller is stronger” effect. Specimens used in accelerated material testing campaigns must reflect bulk material performance to enable engineering scale material property measurement. The objective of this research project was to determine if engineering scale mechanical behavior—the yield stress—could be measured with micro-tensile test samples smaller than traditional standard testing geometries. The relationship between yield stress and sample size was explored with two different nuclear-relevant structural materials: Zircaloy-4 and tungsten. Mechanical testing of both metals demonstrated decreasing yield stress values with increasing sample gauge size across three different sizes. Yield stress values from the largest gauge size, fabricated with a femto-second laser ablation system, approach bulk material yield stress values reported in published literature. Preliminary analysis of the tungsten samples indicates the yield stress value depends on the grain characteristics within the gauge section, in addition to the gauge size. Accompanying modeling efforts, including response surface generation and crystal plasticity approaches, further demonstrated that the size of the sample gauge section alone cannot explain the change in yield stress values.