Behavior of YSZ (High Y2O3 Content) Layer on Inconel to Electro-Chemical Corrosion

The high yttria content of a stabilized zirconia (YSZ) (38 wt% Y₂O₃) coating was deposited by atmospheric plasma spraying (APS) from Metco 207 powders on an Inconel 718 (Ni-based superalloy) substrate. As a metal coating connection, a layer of cermet powder (Ni-20% Al-410NS) was used before the ceramic layer deposition. The electro-chemical corrosion resistance of these materials was tested using Inconel cylinders with a diameter of 10 mm and a thickness of 1 mm, with and without the ceramic layer. Linear and cyclic measurements were obtained in H₂SO₄ electrolyte media at pH = 2. Electro-impedance spectroscopy (EIS) experiments were performed on the sample covered with the ceramic layer to evaluate the interface behavior. Scanning electron microscopy (SEM), along with equipment to determine chemical composition, and an energy dispersive spectrometry (EDS) detector were used to characterize the material surface before and after corrosion tests. It was observed that the corrosion resistance of Inconel was influenced by the bonding layer and the ceramic coating.