Fatigue Experiment and Failure Mechanism Analysis of Aircraft Titanium Alloy Wing–Body Connection Joint

Taking the titanium alloy wing-body connection joint at the rear beam of a certain type of aircraft as the research object, this study analyzed the failure mechanism and verified the structural safety of the wing-body connection joint under actual flight loads. Firstly, this study verified the validity of the loading system and the measuring system in the test system through the pre-test, and the repeatability of the test was analyzed for error to ensure the accuracy of the experimental data. Then, the test piece was subjected to 400,000 random load tests of flight takeoffs and landings, 100,000 Class A load tests, and ground-air-ground load tests, and the test piece fractured under the ground-air-ground load tests. Lastly, the mechanism analysis and structural safety verification of the fatigue fracture of the joints were carried out by using a stereo microscope and scanning electron microscope. The results show that fretting fatigue is the main driving force for crack initiation, and the crack shows significant fatigue damage characteristics in the stable growth stage and follows Paris' law. Entering the final fracture region, the joint mainly experienced ductile fracture, with typical plastic deformation features such as dimples and tear ridges before fracture. The fatigue crack growth behavior of the joint was quantitatively analyzed using Paris' law, and the calculated crack growth period life was 207,374 loadings. This result proves that the crack initiation life accounts for 95.19% of the full life cycle, which is much higher than the design requirement of 400,000 landings and takeoffs, indicating that the structural design of this test piece is on the conservative side and meets the requirements of aircraft operational safety. This research is of great significance in improving the safety and reliability of aircraft structures.