Graphitic carbon nitride supported metal-free heterostructure embedded with carbon quantum dots and PEDOT as electrodes for supercapacitors

• Improved interconnectivity with CQD and electronic property with PEDOT of g-C 3 N 4 . • Supercapacitor achieved a specific capacitance of 109.5 F/g at a current density of 0.2 A/g. • Dual EDLC and redox behavior stable at different scan rates and current densities. • Findings suggest improved energy storage capabilities (E=14.6 Wh kg −1 & P=1.4 kW kg −1 ). Energy storage technologies enable the efficient storage and release of energy, providing essential flexibility and stability to power grids worldwide. Supercapacitors are advanced energy storage systems capable of rapidly storing and releasing large amounts of electrical energy, offering long cycle life and high-power density. Herein, a carbon quantum dot (CQD) dispersed 2D graphitic carbon nitride (g-C 3 N 4 ) nanocomposite was deposited with poly(3,4-ethylene dioxythiophene) (PEDOT) by an electrodeposition technique. The structural, morphological, functional group, and elemental characteristics of the synthesized materials were analyzed using X-ray diffraction (XRD), scanning electron microscopy (SEM), Fourier transform infrared (FTIR) spectroscopy and X-ray photoelectron spectroscopy (XPS). An electrochemical study of electrode materials named g-C 3 N 4 , g-C 3 N 4 -CQD and g-C 3 N 4 -CQD/PEDOT (GCP) composites was performed. The GCP electrode-based symmetric supercapacitor device exhibited a specific capacitance (C s ) of 109.5 F g −1 at a current density of 0.2 A g −1 in 1 M H 2 SO 4 . Herein, the prime novelty is the incorporation of CQDs as spacers between g-C 3 N 4 layers, which substantially improved the surface area, providing potential benefits such as higher energy density and greater stability for supercapacitors. The supercapacitor device utilizing GCP demonstrated an energy density of 14.6 Wh kg −1 at a power density of 1.4 kW kg −1 , operating at a current density of 0.2 A g −1 . The improved electrochemical performance of the hybrid electrode materials is ascribed to the combined effect of the faradaic PEDOT and the non-faradaic CQDs incorporated into the g-C 3 N 4 matrix.