Effects of Zn and Ca on the deformation texture evolution of Mg–Zn–Ca alloys at elevated temperatures

This work utilized crystal plasticity simulations and experimental thermo-mechanical processing to examine how Zn and Ca content affects texture evolution in Mg–Zn–Ca alloys during simulated hot rolling. Four different compositions were studied: unalloyed Mg and three Mg alloys of ZX0p50 (Mg- 0.5 wt% Zn- 0.1 wt% Ca), ZX30 (Mg-3 wt% Zn- 0.1 wt% Ca), and ZX31 (Mg-3 wt% Zn- 0.3 wt% Ca). Multi-pass Gleeble experiments simulated hot rolling using plane strain conditions. Unalloyed Mg developed a strong basal texture, while the addition of Zn and Ca significantly weakened the texture in ZX30 and ZX31; this reduction was not seen in ZX0p50. Notably, ZX31 exhibited a split basal texture aligned with the rolling direction. Crystal plasticity simulations revealed that the weaker basal texture in ZX30 and ZX31 resulted from reduced activation of basal and twinning modes compared to unalloyed Mg and Zx0p50. Increased Zn and Ca content raised the ratios of basal to pyramidal <c+a> critical resolved sheer stress (CRSS) and twin to pyramidal <c+a> CRSS, enhancing pyramidal <c+a> slip activity and weakening the basal texture. Extension twinning played a critical role in texture development during the first deformation pass. In unalloyed Mg and ZX0p50, twinning led to a strong basal texture, while ZX30 and ZX31 had weak basal textures that increased only slightly with further deformation. The split basal poles simulated in ZX31 were consistent with the experimental findings, highlighting the interplay between alloy composition and texture evolution.