Properties evaluation of terrazzo tiles produced for external use using a fine aggregate from a domestic waste incineration plant

The increasing amount of incineration ash raised significant environmental concerns, particularly regardingwaste disposal and pollution. To address these issues and promote sustainable development, this study explored the production of terrazzo tiles using a fine aggregate of waste incineration bottom ash (WIBA) and aternary binder of cement, fly ash, and hydrated lime. The findings revealed that the substitution of cement withhydrated lime at an optimal level (i.e., 1% by weight) enhanced the flexural and compressive strengths whilereducing the surface water absorption of the terrazzo tiles. The surface abrasion resistance remained relativelyunchanged due to the consistent use of the same surface material across samples. Observation of scanningelectron microscope images further confirmed the obtained engineering properties of the terrazzo tiles. As aresult, the terrazzo tiles met the Vietnamese National standard requirements for external use, further indicatingtheir suitability for various applications in construction. This study found that the terrazzo tiles produced usinga mixture of 13% cement, 1% hydrated lime, 10% fly ash, and 76% WIBA earned the lowest surface waterabsorption of 2.56% and the highest flexural and compressive strengths of 3.86 and 21.37 MPa, respectively.Whereas, the surface abrasion of the sample was recorded at 0.241 g/cm2, making it an optimal choice for practical use in construction.