Electrolessly Deposited Cobalt–Phosphorus Coatings for Efficient Hydrogen and Oxygen Evolution Reactions

Hydrogen production via water splitting is one of the latest low-cost green hydrogen production technologies. The challenge is to develop inexpensive and highly active catalysts. Herein, we present the preparation of electrocatalysts based on cobalt–phosphorus (Co-P) coatings with different P contents for hydrogen and oxygen evolution reactions (HER and OER). The Co-P coatings were deposited on the copper (Cu) surface using the economical and simple method of electroless metal deposition. The morphology, structure, and composition of the Co-P coatings deposited on the Cu surface were studied via scanning electron microscopy (SEM) and energy-dispersive X-ray spectroscopy (EDX), while their activity for HER and OER in 1 M KOH was investigated using linear sweep voltammetry (LSV) and chrono-techniques. It was found that the catalyst activity for both HER and OER depends on the P content of the catalyst and varies based on the highest efficiency for each reaction. The Co-P coating with 11 wt% P exhibited the lowest overpotential value of 98.9 mV for the HER to obtain a current density of 10 mA cm−2 compared to the Co-P coatings with 8, 5, 1.6, and 0.4 wt% P (107.6, 165.9, 218.2, and 253.9 mV, respectively). In contrast, the lowest OER overpotential (378 mV) was observed for the Co-P coating with 8 wt% P to obtain a current density of 10 mA cm−2 as compared to the Co-P coatings with 5, 11, 1.6, and 0.4 wt% P (400, 413, 434, and 434 mV, respectively). These results suggest that the obtained catalysts are suitable for HER and OER in alkaline media.