The Enhanced Electrochemical Properties of Lithium-Rich Manganese-Based Cathode Materials via Mg-Al Co-Doping

Due to the advantages of high capacity, low working voltage, and low cost, lithium-rich manganese-based material (LMR) is the most promising cathode material for lithium-ion batteries; however, the poor cycling life, poor rate performance, and low initial Coulombic efficiency severely restrict its practical utility. In this work, the precursor Mn2/3Ni1/6Co1/6CO3 was obtained by the continuous co-precipitation method, and on this basis, different doping levels of aluminum–magnesium were applied to modify the electrode materials by high-temperature sintering. The first discharge capacity can reach 295.3 mAh·g−1 for the LMR material of Li1.40(Mn0.666Ni0.162Co0.162Mg0.005Al0.005)O2. The Coulombic efficiency is 83.8%, and the capacity retention rate remains at 84.4% after 300 cycles at a current density of 1 C for the Mg-Al co-doped LMR material, superior to the unmodified sample. The improved electrochemical performance is attributed to the increased oxygen vacancy and enlarged lithium layer spacing after trace magnesium–aluminum co-doping, enhancing the lithium-ion diffusion and effectively mitigating voltage degradation during cycling. Thus, magnesium–aluminum doping modification emerges as a promising method to improve the electrochemical performance of lithium-rich manganese-based cathode materials.