Macro-Mesoscopic Failure Mechanism Based on a Direct Shear Test of a Cemented Sand and Gravel Layer

In order to explore the influence of different layer treatment methods on the macro- and meso-mechanical properties of cemented sand and gravel (CSG), in this paper, the shear behavior of CSG material was simulated by a three-dimensional particle flow program (PFC3D) based on the results of direct shear test in the laboratory. In shear tests, untreated CSG samples with interface coating mortar and chiseling were used, and granular discrete element software (PDC3D 7.0) was used to establish mesoscopic numerical models of CSG samples with the above three interface treatment methods, in order to reveal the effects of interface treatment methods on the interface strength and damage mechanism of CSG samples. The results show that, with the increase in normal stress, the amount of aggregate falling off the shear failure surface increases, the bump and undulation are more obvious, and the failure mode of the test block is inferred to be extrusion friction failure. The shear strength of the mortar interface is 40% higher than that of the untreated interface, and the failure surface is smooth and flat under different normal stresses. The shear strength of the chiseled interface is 10% higher than that of the untreated interface, and the failure surface fluctuates significantly under different normal stresses. Through the analysis of the fracture evolution process in the numerical simulation, it is found that the fracture of the sample at the mortar interface mainly expands along the mortar–aggregate interface and the damage mode is shear slip. However, the cracks of the samples at the gouged interface are concentrated on the upper and lower sides of the interface, and the damage mode is tension–shear. The failure mode of the samples without surface treatment is mainly tensile and shear failure, and the failure mode gradually changes to extrusion friction failure.