Unveiling the Potential of Civil Briquette Furnace Slag as a Silico–Aluminon Additive in Alkali-Activated Materials

Civil briquette furnace slag (FS), as a type of industrial solid waste, is not currently being recycled as a resource by the building materials industry. This study focuses on the potential of FS in the formulation of alkali-activated materials (AAMs) compared with calcium carbide slag (CS). This study encompasses three distinct AAM systems: alkali-activated fly ash alone (AAFA), fly ash-slag powder blends (AAFB), and slag powder alone (AABS). Electrical conductivity, fluidity, drying shrinkage, and flexural and compressive strengths were also assessed. Advanced characterization techniques, including SEM-EDS, XRD, FTIR, and TG-DSC, were utilized to examine the morphology, mineralogy, and reaction products. Despite the chemical similarity between FS and CS, FS exhibits limited active chemical components (SiO₂, Al₂O₃, CaO, and MgO) and primarily functions as a physical filler, and thus lacks the chemical binding properties of CS. FS has a positive effect on the long-term compressive strength of the AABS system but not on the AAFA and AAFB systems. The NaOH-activated SP mortar sample with 20% FS reaches a compressive strength of 29.8 MPa at 360 days. The binding strength in AAMs incorporating FS is predominantly attributed to the gel formation within the alkali-activated matrix. This research offers valuable insights into the strategic use and substitution of CS, FS, and other silico-aluminon additives within the context of AAMs development.