Correlative analysis of CsPbBr2Hal (Hal = Cl, Br, I) meltcrystallization paramete

Abstract — Metal halide perovskites (MHPs) are an exciting research topic as they have the potential to make solar cells that are both more efficient than current siliconbased designs and have a wider range of applications. In this work the crystallization of CsPbBr2Hal (Hal = Cl, Br, I) halide perovskite melts were studied by the differential thermal analysis method. It was established that the crystallization of CsPbBr2Hal (Hal = Cl, Br, I) melts can be “hot” (i.e., at temperatures above the point of the alloy’s start-melting temperature) or with supercooling. The replacement of the bromine atom with another halogen atom leads to a shift of the dwell temperature range, at which “hot” crystallization takes place, from 830-846 K for CsPbBr3 to 807-832 K for CsPbBr2Cl and 741-768 K for CsPbBr2I. The activation energy of “hot” crystallization decreases in the same order. A linear dependence between the pre-exponential factor (ln(𝑽𝑽𝒄𝒄𝒄𝒄𝒄𝒄𝒔𝒔𝒕𝒕 𝟎𝟎 )) and the activation energy (Ea) of the crystallization process is revealed from the experimental data, proving the compensation effect.