Pressureless sintering of lithium hydride

Lithium Hydride is a material of growing importance for addressing technological challenges related to nuclear fusion, long-term human space travel, and thermal energy storage. Pressureless sintering provides a straightforward, scalable approach to produce dense LiH parts of all sizes and shapes. Pressed LiH green compacts were sintered at heating rates from 2.5 to 20 °C/min to 650 °C, yielding densities up to 96 ± 1.4 %, with densification initiating at 500 °C. A validated master sintering curve was constructed with a sintering apparent activation energy of 135 kJ/mol. X-ray diffraction and simultaneous thermal analysis revealed Li 2 O formation from 300 – 550 °C and decomposition of LiH into Li metal at 550 °C, each reflected as deviations in the master sintering curve. Computed tomography after thermal treatment to 550 °C showed the formation of corrosion products, and after thermal treatment to 650 °C LiH reduction to Li most significantly at exposed surfaces. • Pressureless sintering of Lithium Hydride to 650 °C can yield 96 % density. • A master sintering curve (MSC) for LiH is reported with an activation energy of 135 kJ/mol. • X-ray diffraction, simultaneous thermal analysis, and X-ray computed tomography captured the effects of heating rate on sintering and corrosion.