Oxidation Behavior and Creep Resistance of Cast MC-Strengthened CoNiFeMnCr HEAs at 1100 °C

The reinforcement of cast Cantor’s-type high-entropy alloys by MC carbides and their effect on the hot oxidation behavior were investigated. Three equimolar CoNiFeMnCr alloys without or with carbon and with either hafnium or tantalum were elaborated. Their as-cast microstructures were specified. Oxidation tests were carried out in air at 1100 °C. Flexural creep tests were performed at 1100 °C at 10 MPa. The carbide-free CoNiFeMnCr alloy was single-phased. The version with Hf and C added and the one with Ta and C added contained interdendritic eutectic script HfC and TaC carbides, respectively. After oxidation for 50 h at 1100 °C, all alloys were covered by a (Cr,Mn)2O3 scale with various proportions of Cr and Mn. HfO2 or CrTaO4 also formed. Oxidation resulted in a deep depletion in Cr and in Mn in the subsurface. Oxidation is much faster for the three alloys by comparison with chromia-forming alloys. Their bad oxidation behavior is obviously due to Mn and protection by coating is to be considered. The creep deformation of the carbide-free CoNiFeMnCr alloy was very fast. The creep resistance of the two versions reinforced by either HfC or TaC deformed much slower. The addition of these MC carbides led to a deformation rate divided by five to ten times. Now, creep behavior comparisons with commercial alloys are to be conducted. They will be performed soon.