Formation of Heterogeneous Nucleation of B2-NiAl in Hot Rolled Fe-Mn-Al-C Plate: A Novel Composition and Processing Route for Lightweight High Strength Steel Containing Nickel

In this study, a novel lightweight Fe-Mn-Al-C steel composition and thermomechanical processing route was developed to produce a fully austenitic microstructure with a uniform intragranular dispersion of B2-NiAl precipitation in order to overcome the significant challenge of strengthening hot-rolled Fe-Mn-Al-C steels while retaining toughness. The new composition and processing methods allow for the processing of ultrahigh-strength Fe-Mn-Al-C steel containing nickel as thicker gauge plate for a multitude of new automotive and structural applications where lightweighting is critical. The composition investigated in this study was a fully austenitic Fe-21Mn-9Al-1C-8Ni wt% steel. Two hot rolling methods were investigated: the first procedure involved lower temperature rolling cycles to precipitate B2-NiAl during hot rolling and reheating. The second method involved higher temperature rolling to precipitate B2-NiAl after thermomechanical processing during a short isothermal treatment. The lower temperature rolling produced plate with an ultimate tensile strength of 1120 MPa and a Charpy V-Notch (CVN) toughness of 24 J at −40 °C. After the high temperature rolling procedure, precipitation of B2-NiAl through a subsequent precipitation hardening step resulted in reduced B2-NiAl size and improved the ultimate tensile strength above 1300 MPa. The two novel processing routes of a single composition can be performed with current manufacturing capabilities to produce hot rolled plate strengthened by B2-NiAl precipitation to various hardness (ranging from 33 to 41 HRC) and strength levels (ranging from 1100 to 1320 MPa ultimate tensile strength) while retaining 22–27% elongation.