Calcination Temperature Impacting the Structure and Activity of CuAl Catalyst in Aqueous Glycerol Hydrogenolysis to 1,2-Propanediol

Abstract This study investigated the impact of calcination temperature on the structural properties of CuAl catalyst which was found to be a robust nano-structured catalyst calcined directly without ramping at 400 °C and performed exceedingly well for aqueous phase hydrogenolysis of glycerol. Various samples of CuAl catalysts were prepared by co-precipitation at Cu: Al molar ratio 1:1 and were calcined at different temperatures (300–1000 °C). The obtained catalysts were reduced at 200 °C before their activity testing for glycerol hydrogenolysis reaction. To correlate the structure-activity, the catalysts were thoroughly characterized by XRD, XPS, BET, TEM, H 2 -TPR, NH 3 -TPD, and pyridine FTIR. It was observed that with an increase in calcination temperature from 300 to 700 °C, the glycerol conversion also increased from 47 to 55% with 93% selectivity to 1,2-PDO. The better performance of these catalysts was mainly related to the predominant presence of Brønsted acid sites, an appropriate ratio of the Cu 0 to CuAl 2 O 4 + CuO (0.33) and CuAl 2 O 4 to CuO phases (0.35), the existence of Cu 2 O phase and the smaller Cu 0 particle size. It was shown that altering the ramping rate for the calcination temperature of 400 °C impacted the catalytic activity. The CuAl-400 (DC) (direct calcined) catalyst exhibited a maximum glycerol conversion of 60%.