The surface oxidation effect on photocurrent in WSe1.95Te0.05 nanosheets
Surface oxidation effect on photocurrent responsibility was detected in WSe<sub>1.95</sub>Te<sub>0.05</sub> nanosheets, and the photocurrent response depends on the light wavelength. It is enhanced at the wavelength of 405 nm, while showing no change at the wavelength of 532 nm and suppressed at the wavelength of 808 nm. The incident photon-to-current efficiency (IPCE) is expected to increase at 405 nm wavelength, remain unchanged at 532 nm wavelength, and decrease at 808 nm wavelength. Therefore, WO<sub>3</sub> contributes to the intrinsic properties. The trend of photocurrent change after half-year exposure corresponds to the absorbance change from pristine WSe<sub>1.95</sub>Te<sub>0.05</sub> to WO<sub>3</sub>. The wavelength-dependent photocurrent responsibility is understood as the wavelength-dependent IPCE of WO<sub>3</sub> that is from the surface-oxidized WSe<sub>1.95</sub>Te<sub>0.05</sub>.
Authors
- Ruei‐San Chen (ORCID: https://orcid.org/0000-0003-0042-2521)
- Yue-Cheng Hsieh
- Tzu-Yueh Tu
- Mitch M. C. Chou (ORCID: https://orcid.org/0000-0003-0113-7191)
- Shiu‐Ming Huang (ORCID: https://orcid.org/0000-0002-0085-1353)
- Pin-Cing Wang (ORCID: https://orcid.org/0000-0001-5162-7370)
- Changyu Li (ORCID: https://orcid.org/0000-0001-8656-0428)
- Haoting Wu
Institutions
- National Sun Yat-sen University (TW)
- National Taiwan University of Science and Technology (TW)
- National Cheng Kung University (TW)
Publication Details
- Journal
- iScience
- Published
- 2024-11-22
- DOI
- https://doi.org/10.1016/j.isci.2024.111461
- Citations
- 3
- Primary Topic
- 2D Materials and Applications
- Type
- article
- Field-Weighted Citation Impact
- 0.35
Funders
- National Sun Yat-sen University
- Ministry of Science and Technology, Taiwan