VANCOMYCIN ELUTION KINETICS FROM ANTIBIOTIC AUGMENTED ALLOGRAFT AND RESORBABLE SYNTHETIC BONE FILLER SUPERIOR TO ANTIBIOTIC AUGMENTED BONE CEMENT: AN IN VITRO STUDY OVER 42 DAYS

Abstract Background The aim of the present experimental study was to analyse vancomycin elution kinetics of nine bone fillers used in orthopaedic and trauma surgery over 42 consecutive days. Methods Two allograft bone chips (carriers 1 and 2), a calcium-sulfate matrix (carrier 3), a hydroxyapatite/calcium-sulphate composite (carrier 4), four bone cements (carriers 5-8) and a pure tricalcium phosphate matrix (carrier 9), either already contained vancomycin, or were mixed with it following manufacturer's recommendations. Over 42 days, half of elution medium was substituted by the same amount of PBS at 9 distinct time points. Vancomycin concentration in obtained samples were measured with a kinetic microparticle immunoassay, and masses consecutively calculated. To enhance comparability between carriers analysed, vancomycin mass released related to overall mass within each probe was determined. Notably, elution kinetics of carriers 1 to 4 have been published previously. Results All carriers initially released high vancomycin masses, followed by constant reduction later into the experiment. Mean initial vancomycin masses released after 4 hours were highest for carriers 1 (337.7 ± 76.2 mg), 9 (68.4 ± 4.9 mg), and 2 (49.0 ± 54.6 mg). From prefinal (35 days) to last measurement (42 days) carriers 2 (8.6 ± 4.8 mg), 1 (2.4 ± 1.0 mg), and 5 (0.1 ± 0.1 mg) had released highest vancomycin masses. Notably, all five bone cements tested only released a small percental amount of their total mass up to the last measurement (42 days; 2.1% – 9.3%), whilst allografts and resorbable synthetic bone fillers discarded high percental values (22.5% – 79.2%). Conclusions Elution kinetics differ between 9 antibiotic-loaded bone fillers, with high vancomycin masses released by allografts and resorbable bone fillers over time. Transferred to clinical practice, these may be favoured over bone cements in case prolonged and high antibiotic release is warranted rather than mechanical stability.