Magnetooptical gyrotropic effects in nanosized BiYIG films and diamagnetic YAG substrates

Magneto-optical gyrotropic Faraday and Kerr effects are studied in the BiY2Fe5O12 films with thicknesses ranging from 16 to 55 nm, in the wavelength range of 295 nm < λ < 830 nm (4.2–1.5 eV), and under magnetic fields of up to 1.2 T. It is shown that films produced by ac magnetron sputtering on the single-crystalline diamagnetic yttrium aluminum garnet substrates Y3Al5O12 (001) exhibit high structural and magneto-optical quality. The Verdet constant for diamagnetic Y3Al5O12 is determined, and the magnitude of the Kerr effect is estimated for the polished substrate. It is shown experimentally that for a substrate with diffusely reflective backside, the Kerr effect is about zero, except in the high-energy region. For all BiY2Fe5O12 films investigated, in the saturating magnetic fields of approximately 0.16–0.2 T, the value of specific Faraday rotation reaches 20 deg/μm (200 000 deg/cm), while the value of the Kerr effect reaches approximately 20 min (5.8 mrad). The critical thickness of the film–substrate interface was estimated, highlighting variations in the Kerr effect spectra associated with a decrease in the Bi content in thin films with the thicknesses of below 27 nm.