Multiple Preheating Processes for Suppressing Liquefaction Cracks in IN738LC Superalloy Fabricated by Electron Beam Powder Bed Fusion (EB-PBF)

In additive manufacturing, controlling hot cracking in non-weldable nickel-based superalloys poses a significant challenge for forming complex components. This study introduces a multiple preheating process for the forming surface in electron beam powder bed fusion (EB-PBF), employing a dual-band infrared surface temperature measurement technique instead of the conventional base plate thermocouple method. This new approach reduces the temperature drop during forming, decreasing surface cooling by 28.6% compared to traditional methods. Additionally, the precipitation of carbides and borides is reduced by 38.5% and 80.1%, respectively, lowering the sensitivity to liquefaction cracking. This technique enables crack-free forming at a lower powder bed preheating temperature (1000 °C), thereby improving the powder recycling rate by minimizing powder sintering. Microstructural analysis confirms that this method reduces low-melting eutectic formation and alleviates liquefaction cracking at high-angle grain boundaries caused by thermal cycling. Consequently, crack-free IN738 specimens with high-temperature durability were successfully achieved, providing a promising approach for the EB-PBF fabrication of crack-resistant IN738 components.