Ambipolar Transport in Polycrystalline GeSn Transistors for Complementary Metal-Oxide-Semiconductor Applications

Group-IV alloy GeSn is a promising material for electronic and optoelectronic applications due to its compatibility with both Si substrates and established Si fabrication processes. This study focuses on polycrystalline GeSn (10% Sn), which offers a cost-effective, large-area, and versatile alternative to epitaxial GeSn. We demonstrate ambipolar transport behavior in polycrystalline GeSn thin film transistors, achieving electron and hole field-effect mobilities reaching up to 0.05 cm<sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sup>/Vs and 2.05 cm<sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sup>/Vs, respectively. Through temperature-dependent analysis, we elucidate the underlying mechanism of this phenomenon, which we attribute to quantum tunneling between the Schottky barrier contact and the channel, as well as potential barriers between the grain boundaries of this polycrystalline film, thereby advancing the understanding of polycrystalline GeSn's electrical properties. This work highlights the potential of ambipolar transport as a technique to employ towards the development of GeSn complementary metal-oxide-semiconductor field-effect transistors, promising to simplify and reduce the cost of GeSn manufacturing processes for edge computing and sensing applications.