Effect of Electrofriction Treatment on Microstructure, Corrosion Resistance and Wear Resistance of Cladding Coatings

In recent years, the issue of increasing the wear resistance of the working bodies of agricultural machinery designed for cutting and breaking the soil has received special attention. The surface layers of working bodies of agricultural machinery during operation are subjected to intensive abrasive wear, which leads to rapid wear of equipment and a reduction in its service life. The induction cladding method using materials such as Sormait-1 is widely used to increase the wear resistance of tool working surfaces. However, after coating, additional heat treatment is required to improve the physical and mechanical properties of the material and increase its durability. In electrofriction technology (EFT) hardening, the surfaces of the parts are subjected to melting under the influence of electric arcs. In this work, three types of surface treatment of L53 steel have been investigated: induction cladding using Sormait-1, electrofriction treatment, and a combination of induction cladding followed by electrofriction treatment. The microstructure was analyzed using optical microscopy and scanning electron microscopy. Erosion and abrasion tests were carried out in accordance with ASTM G65 and ASTM G76-04 international standards to evaluate the wear resistance of the materials under mechanical stress. A dendritic structure was formed after the induction cladding of the Sormait-1 material, but subsequent electrofriction treatment resulted in a reduction of this dendritic structure, which contributed to an increase in the hardness of the material. However, the highest hardness, reaching 965 HV, was recorded after electrofriction treatment of L53 steel. This is explained by needle martensite in the structure, which is formed as a result of quenching. Further, the influence of structural characteristics and hardness on erosion and abrasion wear resistance was examined. The analysis showed that the material microstructure and hardness have a decisive influence on the improvement of wear resistance, especially under conditions of intensive erosion and abrasive friction.