Transmission and Reflection Properties of Iron Pyrite-Epoxy Resin Composite for Electromagnetic Applications

This study examines the electromagnetic properties of a composite material composed of iron pyrite (FeS₂) and epoxy resin, mixed in a 3:2 weight ratio to create a 10 cm³ cube. The research analyzes transmission and reflection coefficients and band gap parameters to determine its viability as an antenna substrate for electromagnetic wave applications. The composite displays a tunable band gap of 1.3 eV, enabling selective absorption and emission of electromagnetic radiation. The transmission coefficient achieved 90% throughout a frequency range of 1 GHz to 15 GHz, whilst the reflection coefficient was measured at 10%, significantly reducing reflecting losses. The epoxy resin binder was essential for preserving structural integrity and augmenting the dielectric characteristics of the composite, thereby raising transmission efficiency. UV-Vis spectroscopy showed an absorption value of 0.875% at the band gap, indicating efficient interaction with UV energy. The S21 transmission coefficient ranged from -10 dB to -80 dB, with a maximum of -40 dB at 6 GHz, indicating strong energy transfer capability for antenna applications. The S21 values exhibited negligible signal attenuation between 2 GHz and 7 GHz, indicating the material's exceptional suitability for antenna substrates necessitating dependable transmission. The S11 reflection coefficient varied from -5 dB to -55 dB, with substantial decreases between 4 GHz and 14 GHz, when reflection decreased to -45 dB, signifying little signal reflection at essential frequencies. The results underscore the composite's appropriateness for applications requiring high transmission efficiency, little reflection, and effective engagement with electromagnetic waves, especially as an antenna substrate. Measurements were performed using a vector network analyzer (VNA) to obtain the S11 and S21 characteristics, underscoring the material's potential in sophisticated electromagnetic applications.