Improving comprehensive properties of Cu−11.9Al−2.5Mn shape memory alloy by adding multi-layer graphene carried by Cu51Zr14 inoculant particles

In order to improve the comprehensive properties of the Cu−11.9Al−2.5Mn shape memory alloy (SMA), multilayer graphene (MLG) carried by Cu 51 Zr 14 inoculant particles was incorporated and dispersed into this alloy through preparing the preform of the cold-pressed MLG−Cu 51 Zr 14 composite powders. In the resultant novel MLG/Cu−Al−Mn composites, MLG in fragmented or flocculent form has a good bonding with the Cu−Al−Mn matrix. MLG can prevent the coarsening of grains of the Cu−Al−Mn SMA and cause thermal mismatch dislocations near the MLG/Cu−Al−Mn interfaces. The damping and mechanical properties of the MLG/Cu−Al−Mn composites are significantly improved. When the content of MLG reaches 0.2 wt.%, the highest room temperature damping of 0.0558, tensile strength of 801.5 MPa, elongation of 10.8%, and hardness of HV 308 can be obtained. On the basis of in-depth observation of microstructures, combined with the theory of internal friction and strengthening and toughening theories of metals, the relevant mechanisms are discussed.