Exploring the potential of CdSe nanostructured thin films for energy conversion and environmental remediation

Abstract The rapid thermal evaporation method was employed to prepare cadmium selenide (CdSe) nanostructured thin films with varying thicknesses on glass and FTO substrates. The films were characterized for their structural, optical, and electrochemical properties. Scanning electron microscope (SEM) analysis revealed inhomogeneous surfaces with particle sizes ranging from 18 to 46 nm. The photocatalytic performance of the CdSe films was evaluated by the degradation of methylene blue (MB) dye under visible light, with varying pH values, achieving a degradation efficiency of 100% at pH 10 after 180 min. Photocurrent density measurements demonstrated the films’ ability to sense visible light. We performed a cyclic voltammetry (CV) measurement and analyzed the CV curves of the CdSe nanostructured thin film electrodes. It clearly shows that the CV curves had a rectangular shape, which suggests that EDLC behavior was present and non-faradaic capacitance was the main type. The photoconversion efficiency measured is 1.4858 at a bias voltage of 0.66 V under illuminated conditions. Nonlinear optical properties were conducted for CdSe nanostructured thin films.