Towards High-Quality Investment Casting of Ti-6Al-4V with Novel Calcium Zirconate Crucibles and Optimized Process Control

The investment casting of titanium and its alloys relies on a high resistance of the crucibles and shell molds in terms of temperature and reactivity. The availability of ceramic crucibles that offer sufficient resistance to the titanium melt enables vacuum induction melting (VIM). CaZrO3 prepared from a mixture of CaO and ZrO2 as a raw material for refractory ceramics shows a high corrosion resistance against metallic melts even under very high temperatures up to 1800 °C. Crucibles and shell molds of CaZrO3 were successfully produced and used in subsequent casting trials. This study is focused on the refractory crucibles suitable for casting Ti-6Al-4V (Ti-64) using a tilt casting machine. In order to evaluate the crucible reaction and, therefore, the quality of the castings, chemical analyses, investigations of the microstructures and hardness measurements were carried out. Careful control of the melting duration is mandatory to avoid crucible reactions that otherwise result in contamination of the cast with oxygen and zirconium. This was achieved by modified coil geometries. Under optimized casting conditions, the oxygen and zirconium impurity limits of ASTM B367-09 for titanium castings were met. Based on the correlations found, optimized casting parameters with regard to material quantity, coil geometry and heating power could be determined in order to provide guidance for a high-quality casting process with VIM.