Effect of shell composition on watertightness and mechanical performance of cement-based capsules used as self-healing additives of cement

The aim of this work is the development of cementitious macro-capsules for self-healing cement and concrete materials. Emphasis is placed on shell properties, including size, thickness, strength, and volume to active component ratio. This enhancement is aimed at protecting the healing agent and ensuring adequate reactivity upon crack formation, surpassing survivability considerations. To this direction, core/shell particles have been produced following the pan-coating method, while different types and concentrations of setting acceleration solutions for the shell stabilization were studied. The formation of core-shell capsules encompasses the formation a spherical core through agglomeration, followed by simultaneous spraying of cement powder and a setting acceleration solution for the shell formation, under continuous rotation. The microstructural characteristics of the shell were studied through scanning electron microscopy (SEM), while the reactivity of the protected core (reactive agent) inside the hardened mortar mixtures was evaluated using thermogravimetric analysis (TGA). Moreover, the crushing load of the capsules under compression and their survivability during mixing process were examined and interpreted in relation to their diameter, circularity, and shell thickness. The results revealed the ability of the encapsulation methodology proposed to tailor the shell properties and modify the capsule properties so as satisfy the requirements of different applications. The use of setting accelerators during shell formation proved essential for enhancing the density and the strength of the shell layer. As a consequence, this leads to macro-scale capsules with elevated survivability rate and core reactivity. • Optimization of microstructural characteristics of the shell and improvement of mechanical performance of the capsules. • Enhancement of fracture load and intact to damaged rate during mixing process. • Evolution of shell microstructure, due to continuous hydration within a period of 28 days. • Study of reactivity of the shell-protected core after 28 days of capsules' exposure in elevated humidity.