Evolution of Microstructural and Mechanical Properties of Alloy 617B During Service on a Key-Component Test Platform at 700 °C

The evolution of the microstructural and mechanical properties of alloy 617B during long-term service on a key-component test platform at 700 °C was systematically investigated. The precipitation behavior and size changes of the M₂₃C₆ and <i>γ</i>' phases were characterized by scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The results showed that carbide M₂₃C₆ precipitated in the form of discontinuous particles, plates, or needles at grain boundaries and within grains, while the <i>γ</i>' phase had a spherical shape and was distributed in a dispersed manner. With prolonged service time, both the M₂₃C₆ and <i>γ</i>' phases gradually coarsened. After 24,000 h of service, the yield strength, tensile strength, and Brinell hardness of alloy 617B significantly increased; however, the impact toughness decreased, accompanied by intergranular embrittlement. The increase in precipitate volume fraction and its contribution to the strength of the alloy were evaluated by a precipitation strengthening model. The coarsening of M₂₃C₆ was identified as the main cause of embrittlement. The findings of this study provide important experimental data and theoretical support for the stability of 617B alloys under long-term high-temperature service conditions.