Investigating the Effect of Nano-Crystalline Cellulose in Nitrile Butadiene Rubber Matrix for Improved Thermo-Mechanical Properties

The escalating demand for sustainable rubber products has spurred research into alternative reinforcing fillers, driven by concerns regarding the detrimental effects of using conventional fillers like carbon black and silica. In this investigation, nano-crystalline cellulose (NCC), derived from micro crystalline cellulose (MCC), sourced from sugarcane bagasse via acid hydrolysis, serves as a bio-filler to reinforce Nitrile Butadiene Rubber (NBR) matrices. NBR-NCC nano-composites were prepared using a two-roll mill, varying NCC from 1–5 parts per hundred rubber matrices, followed by hot press curing. NCC and NBR-NCC nano-composites were characterized using Fourier Transform Infrared Spectroscopy (FTIR), Scanning Electron Microscopy (SEM), curing characteristics, thermo-mechanical testing, thermal aging and motor oil resistance. Chemical interactions between the NCC and NBR matrix were verified with FTIR. The SEM images of the NCC showed a combination of rod-like and spherical morphologies and a homogenous dispersion of NCC in NBR-NCC nano-composites with some agglomeration, notably at higher percentages of NCC. It is shown that the cure time decreases with increasing NCC loading which mimics a shorter industrial production cycle. The results also showed an increase in tensile strength, hardness, oil resistance and a rise in degradation temperature when compared to NBR at approximately 34%, 36%, 38% and 32 °C, respectively, at 3 phr NCC loading. Furthermore, NBR-NCC nano-composites showed a lower decrease in mechanical properties after aging when compared to NBR. The findings of this research suggest that the NBR-NCC nano-composites may find applications in high oil resistance seals and rubber gloves where higher thermal stability is strictly required.