Radiation shielding and energy absorption parameters of SiO2–Na2O–Al2O3- CaO-CaF2 silicate glasses

Glasses with nominal compositions of (68-x) SiO 2 –25Na 2 O–2Al 2 O 3 - xCaO-5CaF 2 (x = 0, 5, 10, 20, representing SiNAlCF1, SiNAlCF2, SiNAlCF3, and SiNAlCF4, respectively) were reported for their gamma-photon shielding and dosimetry functions using theoretical calculations starting with the use of the NIST cross-section library. Several parameters (including the mass attenuation (MAC) and energy absorption coefficient (MEAC), effective atomic number and electron density (Z eff and N eff ), gamma exposure constant (Γ), exposure rate (D r ) and exposure buildup factor (EBF) among others) were estimated for energies within 0.015–15 MeV. The range of MAC for SiNAlCF1, SiNAlCF2, SiNAlCF3, and SiNAlCF4 is 0.0208–5.9944, 0.0210–6.7179, 0 0.0212–7.4460, and 0.0217–8.9164 cm 2 /g, respectively. The values of Z eff and N eff vary within the ranges 10.13–12.74 and 2.98–3.74 (10 23 electron/g) for SiNAlCF1, 10.27–13.42 and 2.98–3.89 (10 23 electron/g) for SiNAlCF2, 10.41–14.03 and 2.98–4.01 (10 23 electron/g) for SiNAlCF3, and 10.71–15.07 and 2.98–4.19 (10 23 electron/g) for SiNAlCF4. The glass with the higher CaO content interacts more with gamma rays and attenuates and absorbs photons better. For 15 mm thick SiNAlCF1-SiNAlCF4, D r is about 3.66, 4.10, 4.56, and 5.47 MR/h, respectively. The addition of CaO thus improves the shielding efficacy of the SiNAlCF glasses in the narrow and broad beam geometry situations. The SiNAlCF glasses, in comparison to some conventional and recently recommended glass shields, contain nontoxic component, are cheaper, and effective (especially at higher gamma-photon energies). they are thus recommended for gamma-ray protection applications in narrow and broad beam shielding scenarios.