Effect of Coating Treatment on the Properties of Extruded Mg-1.0Zn-0.3Zr-1.0Y-2.0Sn Alloys

The impact of fluoride-based coatings on the microstructure and mechanical integrity of extruded Mg-1.0Zn-0.3Zr-1.0Y-2.0Sn alloys was assessed utilizing optical microscopy (OM), scanning electron microscopy (SEM), X-ray diffraction (XRD), immersion testing, electrochemical analysis, and tensile testing. It was observed that the magnesium alloys could be immersed in hydrofluoric acid (HF) for varying durations to achieve coatings of distinct thicknesses, with the coating thickness stabilizing at approximately 8 μm after a 48 h immersion period. The application of the fluoride coating significantly enhanced the corrosion resistance of the alloys, with a corrosion rate (CRH) of 0.13 ± 0.012 mm/y. Upon a 20-day immersion in simulated body fluid (SBF), the degradation rates of the yield strength (YS), tensile strength (UTS), and elongation (EL) for the cast alloys were recorded as 62%, 59%, and 64%, respectively. For the extruded alloys, these rates escalated to 77%, 76%, and 95%. In contrast, the fluorine-coated alloys exhibited significantly lower degradation rates of 28%, 23%, and 39% after a 25-day immersion in SBF. Upon extrusion, the specimens exhibit a diminished corrosion resistance and a more substantial decline in mechanical properties compared to their as-cast state. Upon the application of the coating, there is a discernible reduction in the rate of mechanical property degradation observed in the specimens. This indicates that the fluorinated coating can mitigate the corrosion rate and enhance the corrosion resistance of magnesium alloys.