Investigation and estimation of structural and dielectric properties of chromium-doped cobalt ferrites nano particles

Abstract Nano ferrite materials are of critical importance in meeting the global demand for microwave and electronic devices, as spinel ferrites possess remarkable morphological, structural, and dielectric characteristics. This study investigates chromium-doped ferrite nanoparticles with the chemical composition CoCr x Fe 2-x O 4 (x = 0.00, 0.30, 0.60, and 0.90), synthesize using the sol–gel technique and subjected to annealing at 900 °C. Energy Dispersive x-ray Analysis EDAX patterns confirmed compositional stoichiometry. X- Ray Diffraction analysis reveals that all samples exhibit a cubic crystal structure. Replacing some of the ions with chromium (Cr 3+ ) led to a decrease in the x-ray density form (5.329–5.324). The average crystallite size in the fabricated samples ranged from 46.07 to 31.84 nm, and the lattice parameters decrease from 8.382 to 8.364 Å as the chromium content increase. Infrared spectra show that lower frequency band (ν 2 ) at around 479.69-392 .60 cm –1 and a higher frequency band (ν 1 ) within a range from 611.05–57661 cm –1 a clear indication of spinel structure characteristics. The examination using FE-SEM indicates that the produced materials exhibit porosity and amorphous characteristics. The significant tangent loss observe at lower frequencies suggests that these materials may have potential applications in medium-frequency devices. Consequently, spinel nanoferrites can offer advantages for advanced electronic and microwave technologies.