Copper-induced lattice distortion in Na4Fe3(PO4)2(P2O7) cathode enabling high power density Na-ion batteries with good cycling stability

Na 4 Fe 3 (PO 4 ) 2 P 2 O 7 (NFPP) has attracted attention due to its high theoretical capacity, low cost, and good structure stability for Na-ion batteries. However, its practical application is limited by the low intrinsic electronic conductivity and sluggish ion diffusion kinetics. To tackle those problems, lattice strain engineering by heteroatom doping is applied to tune the local molecular structure and optimize the electrochemical properties of electrode materials. Copper cation (+2) with a smaller ionic radius was chosen to dope at Fe-site in NFPP, and the doping amount was also optimized, illustrating the optimized sample of Na 4 Fe 2.7 Cu 0.3 (PO 4 ) 2 P 2 O 7 (NFPP-0.3Cu) delivered a high capacity of 119.01 mAh g -1 at 1 C (1 C = 129 mA g -1 ) and a high capacity retention of 82.76 % after 3000 cycles at 20 C. Notably, full cells with NFPP-0.3 Cu as cathode and hard carbon as anode delivered a high energy density of 230 Wh kg -1 and a power density of 2280 W kg -1 . The exceptional electrochemical performances are attributed to the modulated electronic structure and abundant lattice defects by Cu-doping. Furthermore, in-situ X-ray diffraction technique and theoretical calculation have jointly proved that the lattice distortions originated from Cu-doping have reduced the band gap of the NFPP-0.3Cu and altered the coordination environment of Fe, shortening the Fe-O and Cu-O bond lengths, significantly enhancing the intrinsic ionic conductivity and the diffusion kinetics of Na + . This work provides new point of views on lattice strain engineering and reaction kinetics of cathode materials in promoting high energy and power density sodium-ion batteries. By doping the Fe site of Na 4 Fe 3 (PO 4 ) 2 P 2 O 7 with Cu of small ionic radius, the lattice of Na 4 Fe 3 (PO 4 ) 2 P 2 O 7 is locally distorted, and the resulting lattice distortion reduces the bandgap, changes the coordination environment of Fe, shortens the bond lengths of Fe-O and Cu-O, and improves the intrinsic electronic conductivity and Na + diffusion kinetics, thus realizing a high-power density sodium-ion battery with good cycling stability.

Authors

Institutions

Publication Details

Journal
Energy storage materials
Published
2024-10-25
DOI
https://doi.org/10.1016/j.ensm.2024.103861
Citations
51
Primary Topic
Advancements in Battery Materials
Type
article
Field-Weighted Citation Impact
10.64
Controls
|||
ALL TIME
JAN
FEB
MAR
APR
MAY
JUN
JUL
AUG
SEP
OCT
article

Copper-induced lattice distortion in Na4Fe3(PO4)2(P2O7) cathode enabling high power density Na-ion batteries with good cycling stability

Shuangqiang Chen, Xinran Qi, Yanbin Shen, Xiaoxian Zhao et al.
51 citations
Energy storage materials
Advancements in Battery Materials
10.64
article

Copper-induced lattice distortion in Na4Fe3(PO4)2(P2O7) cathode enabling high power density Na-ion batteries with good cycling stability

Shuangqiang Chen, Xinran Qi, Yanbin Shen, Xiaoxian Zhao, Baoxiu Hou, Hanghang Dong, Shuaihua Zhang, Hui Shao, Ningzhao Shang, Haiyan Liu, Qingyu Dong, Longgang Wang
article en
51 citations

Abstract

Na 4 Fe 3 (PO 4 ) 2 P 2 O 7 (NFPP) has attracted attention due to its high theoretical capacity, low cost, and good structure stability for Na-ion batteries. However, its practical application is limited by the low intrinsic electronic conductivity and sluggish ion diffusion kinetics. To tackle those problems, lattice strain engineering by heteroatom doping is applied to tune the local molecular structure and optimize the electrochemical properties of electrode materials. Copper cation (+2) with a smaller ionic radius was chosen to dope at Fe-site in NFPP, and the doping amount was also optimized, illustrating the optimized sample of Na 4 Fe 2.7 Cu 0.3 (PO 4 ) 2 P 2 O 7 (NFPP-0.3Cu) delivered a high capacity of 119.01 mAh g -1 at 1 C (1 C = 129 mA g -1 ) and a high capacity retention of 82.76 % after 3000 cycles at 20 C. Notably, full cells with NFPP-0.3 Cu as cathode and hard carbon as anode delivered a high energy density of 230 Wh kg -1 and a power density of 2280 W kg -1 . The exceptional electrochemical performances are attributed to the modulated electronic structure and abundant lattice defects by Cu-doping. Furthermore, in-situ X-ray diffraction technique and theoretical calculation have jointly proved that the lattice distortions originated from Cu-doping have reduced the band gap of the NFPP-0.3Cu and altered the coordination environment of Fe, shortening the Fe-O and Cu-O bond lengths, significantly enhancing the intrinsic ionic conductivity and the diffusion kinetics of Na + . This work provides new point of views on lattice strain engineering and reaction kinetics of cathode materials in promoting high energy and power density sodium-ion batteries. By doping the Fe site of Na 4 Fe 3 (PO 4 ) 2 P 2 O 7 with Cu of small ionic radius, the lattice of Na 4 Fe 3 (PO 4 ) 2 P 2 O 7 is locally distorted, and the resulting lattice distortion reduces the bandgap, changes the coordination environment of Fe, shortens the bond lengths of Fe-O and Cu-O, and improves the intrinsic electronic conductivity and Na + diffusion kinetics, thus realizing a high-power density sodium-ion battery with good cycling stability.

Energy storage materialsVol. 73
Hebei Agricultural University (CN), Wenzhou University (CN), Chinese Academy of Sciences (CN), Yanshan University (CN), Suzhou Institute of Nano-tech and Nano-bionics (CN), State Key Laboratory of Metastable Materials Science and Technology
Affordable and clean energy
Openalex Percentile: Top 1%
Advancements in Battery Materials
10.64
AI Navigator

Ask Laika to Summarize, Analyze, and Connect papers live on the map.

Summarize Papers & Methodologies

Extract key findings, datasets, and comparative methods across publications.

Benchmark Rankings & Visual Analytics

Rank top research institutions, authors, funders, topics, and journals by Field-Weighted Citation Impact (FWCI) and paper volume with instant charts.

Connect Distant Disciplines

Bridge topological clusters on the map to find hidden collaborative intersections.