Pressure-induced formability and degradability of block copolymers composed of poly(1,5-dioxepan-2-one) and poly(L-lactide)

• Rheological behavior under pressure of degradable block copolymers were studied. • The block copolymer showed low-temperature formability. • Enzymatic degradability of the block copolymers was investigated. • Both material properties were depended on chemical structures of block copolymers. An aliphatic polyether/carbonate block copolymer, comprising poly(1,5-dioxepan-2-one) (PDXO, glass transition temperature T g : -38 °C) and poly(L-lactide) (PLLA, T g : 55 °C), evinces remarkable formability under pressure at temperatures significantly below the melting point of PLLA. A quantitative and detailed evaluation of the low-temperature molding of the block copolymer was conducted using a capillary rheometer. The findings reveal that block copolymers with PDXO composition >55 wt% demonstrate a propensity to flow at room temperature under 50 MPa pressure. Consequently, the practice of low-temperature molding serves to mitigate the degradation of polymer chains during the molding process, thereby augmenting recyclability. Furthermore, the enzymatic degradability of the block copolymer was extensively investigated using lipase PS and proteinase K. An interplay between the structure of the block copolymer and the degradation kinetics was explored. The polymeric materials developed, possessing both pressure formability and degradability, hold promising potential as environmentally benign polymers with reduced environmental impact.