Magneto-optic properties of highly Dy3+-doped GeO2-B2O3 glasses for NIR optical applications

• Two series of highly Dy 3+ -doped GeO 2 -B 2 O 3 glasses were successfully fabricated. • Structural and thermal properties of the glasses were investigated. • MO properties of the glasses were investigated at 1550 nm. • The highest Dy 2 O 3 -doped glass exhibited the largest V of −5.36 rad/(T⋅m). • Compositional effect on V was investigated in the studied glasses. Recent progress in the development of optical communication and high power laser systems in the near-infrared (NIR) region (1.5 to 2.0 μm) increased the demand for magneto-optic (MO) devices employing MO materials. These MO materials are required with lower optical absorption coefficients and higher Verdet constants at spectral range of interest. In this study, two series of highly Dy 3+ -doped GeO 2 –B 2 O 3 glasses with and without P 2 O 5 were fabricated using a simple melt-quenching technique. The glasses were characterized through various techniques (Raman, UV–VIS-NIR, and DTA) for the evaluation of characteristic properties with respect to the Dy 2 O 3 concentration and glass composition. Faraday rotation measurement was carried out at 1550 nm to quantify the Verdet constant of the glasses. The Verdet constant values were found to increase linearly with increasing Dy 3+ concentration for both the glass systems. The increase in Dy 3+ concentration and, consequently, the number of unpaired electrons, leads to an increase in the Verdet constant. The GeO 2 -B 2 O 3 glass doped with 30 mol% of Dy 2 O 3 exhibited the highest Verdet constant of −5.36 rad/(T⋅m) at 1550 nm. The glasses exhibited a good optical transparency (>70 %) in the region covering from 400 to 2400 nm. The thermo-physical, optical, and polarizability properties of both glass systems were also investigated. The results indicate that the highly Dy 3+ -doped glasses are attractive for magneto-optics at 1550 nm.