Hydrogen Embrittlement of a Prerolled High‐Mn Steel with Different Cut‐Edge Characteristics

The hydrogen embrittlement behavior of a prerolled Fe–15Mn–0.65C–2Al–2Si high‐Mn steel with various cut‐edge properties is studied via hydrogen precharging and slow strain rate test. In the presence of hydrogen, samples prepared by laser cutting under atmosphere of N 2 exhibit the best total elongation at about 39%. Press blanking produces severe shear deformation, tensile residual stresses, and strain‐induced martensite, resulting in a high risk to hydrogen‐induced cracking. With compressive residual stresses produced from waterjet, corresponding samples exhibit the lowest elongation loss against hydrogen. Despite hydrogen charging, the fracture surfaces show transgranular quasi‐cleavage features, for which mechanical twinning from prerolling plays a critical role. The hydrogen‐enhanced decohesion mechanism accounts for cleavage fracture since hydrogen segregation reduces cohesive stress at twin boundaries.