Physical Properties of Hilti HIT-RE 500 V3 After Irradiation: Slant Shear, Tensile, Flexural, and Compressive

There are various applications in which epoxy adhesives may be used within hot-cell environments. These epoxies currently see limited use within hot cells since it is known that organics see degradation after small doses even as low as 50 kilogray (kGy). These losses in physical property strengths limit the use of these epoxies to non-structural applications. In modern construction, however, the use of epoxies to bond structural components such as rebar or threaded anchors is becoming increasingly prevalent. To employ these types of materials the Idaho National Laboratory (INL) has begun investigating the specific degradation properties of epoxies for use in structural applications in environments where radiation is present. Hilti HIT-RE 500 V3 is used extensively in new construction and renovation projects across the world. The INL has conducted various tests on this epoxy for low dose environments. These tests include tensile, flexural, compression, and slant shear tests following the American Society for Testing Material International (ASTM) standards D638, D790, D695, and C882/882M respectively. Two sample sets for each test were created where the baseline specimens were not irradiated, and another set was irradiated to an accumulated dose of approximately 50-60 kGy. All the samples were destructively tested and analyzed focusing on the change in physical properties, examples of these tests are shown in Figures 1-4. Tensile testing results indicate a 0.9% loss in maximum load capacity, a 0.5% loss in tensile stress at maximum load, a 1.4% loss in tensile strain at break, and a 15% decrease in modulus of elasticity. Flexural testing results display an increase in all the following: 12% in strain at maximum load, 10% in maximum load capacity, 5% in stress at maximum load, and 3% in young’s modulus. The compressive physical properties after irradiation display a 1% increase in maximum load, a 3% decrease in stress at yield, and a 5% decrease in modulus of elasticity. The maximum compressive stress saw no measurable change after irradiation. The slant shear specimens after irradiation displayed a 2% increase in maximum load capacity and maximum compressive stress. Though a structural analysis would have to be completed as is normal for building design the increases and decreases in the measured physical properties indicate that this material may be used for structural applications in low dose hot-cell environments without adhesive failure.