Summary of Alloy 617 and Alloy 709 Elevated Temperature Crack Growth Test Results from the Planned FY24 Crack Growth Test Activities

This report covers the results from crack growth rate testing performed at Idaho National Laboratory in the fiscal year 2024. It includes two creep crack growth rate tests and two creep-fatigue crack growth rate tests. Results are shown for each of these tests, included crack growth measured during the test using direct current potential drop, and measurements based off of the fracture surface. Load line displacement, as well as load, were also collected during the tests. Detailed analysis of the results will continue into the next fiscal year, however, a number of potential improvements to the equipment and testing procedures were identified that will increase testing reliability and throughput, as well as decrease complications with the analysis.