Microstructure-mechanical property relationships of polymer nanocomposite reinforced with lyophilized montmorillonite/carbon nanotubes hybrid particles

Abstract Introducing multi-walled carbon nanotubes (MWCNT) and montmorillonite (MMT) simultaneously into a polymer can significantly enhance its properties. Meanwhile, choosing the best technique to homogeneously disperse these nanohybrid particles in polymers, without agglomerates, is still a challenge. In this study, a hybrid MMT/MWCNT, prepared by lyophilization process, is introduced in polylactide (PLA). Morphology of the resulting nanocomposites displays synergistic relationships of the MMT/MWCNT, facilitating dispersion in PLA. The analysis of transmission electron microscopy (TEM) specific particle densities of PLA0.5hyb, PLA1.0hyb, and PLA2.0hyb shows values of 77, 64, and 35 µm⁻ 2 , respectively. This suggests that MMT platelets are significantly more exfoliated in PLA0.5hyb compared to the other nanocomposites. It also indicates that filler aggregation increases as the MMT/MWCNT concentration increases. Compared to neat PLA, elastic modulus of nanocomposites increased by up to 46 %, demonstrating the reinforcing effect of MMT/MWCNT hybrid nanofillers. The nanocomposites exhibit viscosity, plasticity and damage phenomena, which are significantly decreased because of the MMT/MWCNT incorporation, compared to neat PLA. Furthermore, the viscoelastic properties, analyzed by dynamic thermal-mechanical analysis, record about 27 % increase in the storage modulus of the nanocomposites compared to PLA, indicating the effectiveness of the hybrid MMT/MWCNT in increasing the resistance of PLA/MMT/MWCNT nanocomposite against thermomechanical aggression.