X-ray Diffraction Analysis and Micro Hardness of Ternary Alloy (Ti – 6Al – 4Nb)

This research aims to prepare the ternary alloy (Ti-6Al-4Nb) Using powder technology and studying X-ray diffraction analysis and micro hardness of this alloy. Titanium, aluminum, and niobium, powders were mixed together to homogenize the elements, and then the pressing process was carried out under pressure (5Ton) and for a period of time(60sec) For the purpose of obtaining a cohesive alloy in the form of discs, then the heat Treatment process (annealing) was conducted at different temperatures. (650,750,850,950,1050)˚C for two hours, the structural properties were studied through X-ray diffraction examination (XRD)And studying the mechanical properties by measuring the micro hardness using the Vickers hardness method before and after annealing, the results of the tests showed (XRD)The phases of the basic materials that make up the alloy, as the crystalline structure of titanium appeared to be of the hexagonal stacked type(HCP)As for aluminum, it appeared in a cubic system with concentric faces(FCC) and niobium in a body-centered cubic system (BCC)A new phase also appeared after the annealing process, which is the phase(AlNbTi2)Has a right rhombic crystal structure(Orthorhombic)The results of the micro hardness test (Vickers) showed that the annealing process has a positive effect on improving the mechanical properties, as the hardness value increases when temperatures increase.