Rapid and eco-friendly ultrasonic exfoliation of transition metal dichalcogenides supported on sonogel-nanocarbon black: A non-precious electrocatalyst for hydrogen evolution reaction

Recently, there has been growing interest in replacing expensive platinum-based catalysts with cost-effective non-precious metal alternatives for water electrolysis aimed at hydrogen production. This study introduces an innovative, green, and cost-effective strategy for the development of non-precious electrocatalysts by leveraging sodium alginate-mediated ultrasonic exfoliation to produce transition metal dichalcogenide (TMD) nanosheets. These nanosheets are supported on Sonogel-Carbon electrodes (SGC), providing a novel conductive base for HER catalysis. Using a diverse array of TMD materials, including MoS 2 , MoSe 2 , WS 2 , and WSe 2 , we assess their catalytic activity towards HER. The study demonstrates significantly enhanced HER performance through bulk modification of the electrodes with nanocarbon black (SGC-CB). This enhancement is primarily due to the synergistic effects of improved electron transfer and increased active site availability, facilitated by the unique structural properties of the exfoliated TMD nanosheets and the conductive Sonogel-Carbon substrate. Notably, the optimized MoSe 2NS -SGC-CB configuration achieves an exceptional overpotential of 240 mV at a current density of 10 mA/cm 2 , surpassing conventional bulk catalysts and highlighting the potential of sodium alginate as a viable dispersing agent for the large-scale production of TMD nanosheets. The operational stability and cost-effectiveness of this electrocatalyst, combined with its environmental friendliness, mark a significant step forward in the pursuit of sustainable hydrogen fuel production technologies. • Achieved TMD nanosheets via rapid, green sodium alginate-assisted ultrasonic LPE. • Sonogel carbon (SGC) outperforms conventional carbon support in HER catalysis. • Bulk-modifying SGC with nanocarbon black (CB) further enhances HER performances. • MoSe 2 NS -SGC-CB shows 240 mV overpotential at 10 mA/cm 2 with high stability.