Effect of Laser Powder Bed Fusion Parameters on the Evolution of Melt Pool, Densification, Microstructure, and Hardness in 420 Stainless Steel Parts

Laser powder bed fusion (LPBF) involves depositing, melting, and solidifying metal powder particles layer by layer to create 3D components. In this study, a deep fundamental understanding on how process parameters—laser power, scan speed, and hatch spacing—affect the melt pool, densification, microstructure, hardness, and thermal behavior of 420 stainless steel (420SS) parts produced by such technology is provided. The conducted investigation considers five levels of laser power and hatch spacing, and four scan speeds. Optimal single tracks, based on geometry and profile, are achieved with laser powers between 40 and 80 W and a scan speed of 10 mm s −1 . In the multitrack analysis, it is indicated that a dense, smooth surface is obtained with a hatch spacing of 250 μm, corresponding to an overlapping rate of ≈30%. The 420SS samples show high densification (≈99%) and low surface roughness (≈3.62 μm). The microstructure consisted of martensite laths and retained austenite. The hardness and thermal conductivity of the samples are measured at 540 HV and 15.3 W m −1 K −1 , respectively. In this study, the understanding of the process–structure–property relationships in LPBF of 420SS is expanded.