Effects of Ni cation ratio and sintering temperature on microstructure and electrical properties of NiMnCoO4-based ceramics

Negative temperature coefficient (NTC) thermistors as temperature sensors play an important role in various electrical/electronic devices and are widely applied in the fields such as, automotive sensor modules, home appliances and control applications. The electrical properties of NTC thermistors can be effectively controlled by regulating the content of their chemical components or changing the microstructures. Therefore, this study investigated the effects of Ni cation ratio and sintering temperature on microstructures, crystal structures, and electrical properties of NiMnCoO4-based ceramics. With increasing Ni content, it was found that sinterability of NiMnCoO4-based ceramics was decreased with forming rock-salt phase of NiO, resulting in degrading resistivity. Furthermore, the spinel structures were detected by X-ray diffraction analysis regardless of sintering temperatures. Notably, values of average grain size for sintered samples were increased with increasing sintering temperature. Besides, it was clarified that electrical properties were significantly influenced by average grain size. The room temperature resistivity was increased from approximately 300 kΩ⋅cm for the sintered sample at 1100°C to about 600 kΩ⋅cm for for the sintered sample at 1300oC. On the other hand, the B(25/85) constant was not significantly influenced by the sintering temperature. Accordingly, it is expected that the results of this study are useful for controlling electrical properties of MnCoNiO4-based ceramics.